Mg–O–F nanocomposite catalysts defend against global warming via the efficient, dynamic, and rapid capture of CO₂ at different temperatures under ambient pressure

The utilization of Mg–O–F prepared from Mg(OH)₂ mixed with different wt % of F in the form of (NH4F·HF), calcined at 400 and 500 °C, for efficient capture of CO₂ is studied herein in a dynamic mode. Two different temperatures were applied using a slow rate of 20 mL·min–1 (100%) of CO₂ passing through each sample for only 1 h. Using the thermogravimetry (TG)-temperature-programed desorption (TPD) technique, the captured amounts of CO₂ at 5 °C were determined to be in the range of (39.6–103.9) and (28.9–82.1) mgCO₂·g–1 for samples of Mg(OH)₂ mixed with 20–50% F and calcined at 400 and 500 °C, respectively, whereas, at 30 °C, the capacity of CO₂ captured is slightly decreased to be in the range of (32.2–89.4) and (20.9–55.5) mgCO₂·g–1, respectively. The thermal decomposition of all prepared mixtures herein was examined by TG analysis. The obtained samples calcined at 400 and 500 °C were characterized by X-ray diffraction and surface area and porosity measurements. The total number of surface basic sites and their distribution over all samples was demonstrated using TG- and differential scanning calorimetry-TPD techniques using pyrrole as a probe molecule. Values of (ΔH) enthalpy changes corresponding to the desorption steps of CO₂ were calculated for the most active adsorbent in this study, that is, Mg(OH)₂ + 20% F, at 400 and 500 °C. This study’s findings will inspire the simple preparation and economical design of nanocomposite CO₂ sorbents for climate change mitigation under ambient conditions.