Improved magnetization in sputtered dysprosium thin films

    Research output: Contribution to journalArticle


    View graph of relations

    50nm thick nanogranular polycrystalline dysprosium thin films have been prepared via ultra-high vacuum DC sputtering on SiO2 and Si wafers. The maximum in-plane spontaneous magnetization at T = 4K was found to be µ0MS,4K(C) = (3.28±0.26)T for samples deposited on wafers heated to 350°C with a Neel point of TN(C) = (173±2)K and a ferromagnetic transition at TC(C) = (80±2)K, measured via zero-field-cooled – field-cooled magnetization measurements, close to single-crystal values. The slightly reduced magnetization is explained in the light of a metastable face-centered cubic crystal phase which occurred at the seed interface and granularity related effects, that are still noticeably influential despite an in-plane magnetic easy axis. As deposited samples showed reduced magnetization of µ0MS,4K(A) = (2.26±0.18)T, however their ferromagnetic transition shifted to a much higher temperature of TC(A) = (172±2)K and the antiferromagnetic phase was completely suppressed probably as a result of strain.



    Original languageEnglish
    Article number152001
    Number of pages6
    JournalJournal of Physics D: Applied Physics
    Journal publication date21 Mar 2013
    Issue number15
    Publication statusPublished - 21 Mar 2013

    Research outputs


    ID: 2734865